Mechanical Properties of Calcium and Vanadium

Add ⊕
1 Mechanical
1.1 Density
1.1.1 Density At Room Temperature
1.55 g/cm36.00 g/cm3
Lithium
0.534 40.7
1.1.2 Density When Liquid (at m.p.)
1.38 g/cm35.50 g/cm3
Lithium
0.512 20
1.2 Tensile Strength
NA800.00 MPa
Indium
2.5 11000
1.3 Viscosity
NANA
Mercury
0.001526 0.001526
1.4 Vapor Pressure
1.4.1 Vapor Pressure at 1000 K
25.50 (Pa)NA
Cerium
2.47E-11 121
1.4.2 Vapor Pressure at 2000 K
NA0.23 (Pa)
Tungsten
2.62E-10 774
1.5 Elasticity properties
1.5.1 Shear Modulus
7.40 GPa47.00 GPa
Potassium
1.3 222
1.5.2 Bulk Modulus
17.00 GPa160.00 GPa
Cesium
1.6 462
1.5.3 Young's Modulus
20.00 GPa128.00 GPa
Cesium
1.7 528
1.6 Poisson Ratio
0.310.37
Beryllium
0.032 0.47
1.7 Other Mechanical Properties
NA
Ductile, Malleable