Mechanical Properties of Chromium and Iron
f
Chromium
Iron
Mechanical Properties of Iron and Chromium
Summary
Periodic Table
Facts
Uses
Physical
Chemical
Atomic
Mechanical
Magnetic
Thermal
All
Mechanical Properties
Density
Density At Room Temperature
7.19 g/cm
3
99+
7.87 g/cm
3
99+
Density When Liquid (at m.p.)
6.30 g/cm3
40
6.98 g/cm3
35
Tensile Strength
689.00 MPa
7
11,000.00 MPa
1
Viscosity
Not Available
Not Available
Vapor Pressure
Vapor Pressure at 1000 K
0.00 (Pa)
24
0.00 (Pa)
28
Vapor Pressure at 2000 K
774.00 (Pa)
1
36.80 (Pa)
5
Elasticity properties
Shear Modulus
115.00 GPa
9
82.00 GPa
11
Bulk Modulus
160.00 GPa
11
170.00 GPa
10
Young's Modulus
279.00 GPa
8
211.00 GPa
9
Poisson Ratio
0.21
32
0.29
15
Other Mechanical Properties
NA
Ductile, Malleable, Weldable
Magnetic >>
<< Atomic
Compare Transition Metals
Chromium vs Rhodium
Chromium vs Molybdenum
Chromium vs Cadmium
Transition Metals
Cobalt
Manganese
Tungsten
Iridium
Molybdenum
Rhodium
Transition Metals
Cadmium
Periodi...
|
Facts
|
Uses
|
Physical
Vanadium
Periodi...
|
Facts
|
Uses
|
Physical
Osmium
Periodi...
|
Facts
|
Uses
|
Physical
» More Transition Metals
Compare Transition Metals
Iron vs Tungsten
Periodi...
|
Facts
|
Uses
|
Physical
Iron vs Manganese
Periodi...
|
Facts
|
Uses
|
Physical
Iron vs Iridium
Periodi...
|
Facts
|
Uses
|
Physical
» More Compare Transition Metals